|Dimension:||Interior 160 X 100 X 550cm||Temperature:||NSS ACSS 35℃ ± 1℃|
|Safety Device:||Over-temperature Protection||PH Range:||CASS: 3.0~3.2|
|Uniformity:||≦2. 0℃||Spray Quantum:||1.0~2.0(ml/80cm2/h)|
Customized Programmable Salt Spray Corrosion Chamber for Test Resistance of Durability
Seawater Acidified Test (cyclic) is also referred to as a SWAAT test. Test specimens are placed in an enclosed chamber, and exposed to a changing climate that comprises the following 2 part repeating cycle. 30 minutes exposure to a continuous indirect spray of synthetic seawater solution, prepared in accordance with the requirements of the test standard and acidified (to pH 2.8 to 3.0) by the addition of acetic acid.
This spray is set to fall-out on to the specimens at a rate of 1.0 to 2.0ml/80 cm²/hour. This is followed by 90 minutes exposure to a high humidity climate of above 98%RH. The entire test cycle is at a constant chamber temperature of +49C (may be reduced to +24 to +35C for organically coated specimens). The number of cycle repeats and therefore the test duration is variable.
Most Salt Spray Chambers today are being used NOT to predict the corrosion resistance of a coating, but to maintain coating processes such as pre-treatment and painting, electroplating, galvanizing, and the like, on a comparative basis.
1, Chamber material is made of P.V.C Sheet, sturdily and will not be out of shape.
2, Test chamber is heated from five directions to ensure the temperature is uniformity distributed.
3, Spray nozzle is specially made, enable to spray the salt water with considerable speed, then falls on the surface of samples.
4, Hot and moist air keeps the humidity in the test chamber conforms testing request.
5, High precision P.I.D. temperature controller limits the temperature difference within the range of ±0.1℃.
Please Note Small Type of 60 and 90 do not meet standard of ASTM B117.
|Model (Touch Screen)||HL-60-CS||HL-90-CS||HL-120-CS||HL-160-CS||HL-200-CS|
|Chamber Volume||108 L||270 L||480 L||800 L||1440 L|
|Solution Tank||15L||25 L||40 L|
|Power Supply||AC 220V 50HZ||AC 380V 50HZ|
|Ambient temp. & humid. range||+5℃ ~ +35℃ / <85%RH|
|Testing Temperature||NSS ACSS 35℃±1℃ / CASS 50℃±1℃|
|Air Temperature||NSS ACSS 47℃±1℃ /CASS 63℃±1℃|
|Solution Consistence||NaCl 5%|
|PH Value||NASS ACSS:6.5~7.2 / CASS:3.0~3.2|
|Temperature uniformity||≦2. 0℃|
|Chamber Material||polyvinyl chloride (PVC)|
|Heater||Corrosion-resistant titanium tube|
|Temperature sensor||Platinum Resistance (PT-100)|
|Safety device||Over-temperature protection , leakage protection|
1. The above specifications are for reference only, the actual specifications for the main quotation.
2. Custom made is available according to customers’ special requirements