Laboratory Neutral Salt Spray Corrosion Chamber for Surface Coating Resistance Testing
Brief Introduction:
The salt spray (or salt fog) test is a standardized and popular corrosion test method, used to check corrosion resistance of materials and surface coatings. Usually, the materials to be tested are metallic (although stone, ceramics, and polymers may also be tested) and finished with a surface coating which is intended to provide a degree of corrosion protection to the underlying metal.
Salt spray testing is an accelerated corrosion test that produces a corrosive attack to coated samples in order to evaluate (mostly comparatively) the suitability of the coating for use as a protective finish. The appearance of corrosion products (rust or other oxides) is evaluated after a pre-determined period of time. Test duration depends on the corrosion resistance of the coating; generally, the more corrosion resistant the coating is, the longer the period of testing before the appearance of corrosion/ rust. The salt spray test is one of the most widespread and long established corrosion tests. ASTM B117 was the first internationally recognized salt spray standard, originally published in 1939. Other important relevant standards are ISO9227, JIS Z 2371 and ASTM G85.
Salt Spray Test Chambers offer the most realistic and dependable corrosion test, widely used to test corrosion resistance of automotive, paint, surface coating, chemical, aerospace, electronic, car industry, offshore and defense industries.
Features:
1, Chamber material is made of P.V.C Sheet, sturdily and will not be out of shape.
2, Test chamber is heated from five directions to ensure the temperature is uniformity distributed.
3, Spray nozzle is specially made, enable to spray the salt water with considerable speed, then falls on the surface of samples.
4, Hot and moist air keeps the humidity in the test chamber conforms testing request.
5, High precision P.I.D. temperature controller limits the temperature difference within the range of ±0.1℃.
Technical Specifications:
Please Note Small Type of 60 and 90 do not meet standard of ASTM B117.
Model | HL-60-SS | HL-90-BS | HL-120-NS | HL-160-NS | HL-200-NS | ||
Model (Touch Screen) | HL-60-CS | HL-90-CS | HL-120-CS | HL-160-CS | HL-200-CS | ||
Interior dimensions (mm) |
W | 600 | 900 | 1200 | 1600 | 2000 | |
D | 450 | 600 | 850 | 1000 | 1200 | ||
H | 400 | 500 | 500 | 550 | 600 | ||
Exterior dimensions (mm) |
W | 1130 | 1460 | 2200 | 2600 | 3000 | |
D | 630 | 910 | 1200 | 1450 | 1650 | ||
H | 1070 | 1280 | 1450 | 1550 | 1600 | ||
Chamber Volume | 108 L | 270 L | 480 L | 800 L | 1440 L | ||
Solution Tank | 15L | 25 L | 40 L | ||||
Power Supply | AC 220V 50HZ | AC 380V 50HZ | |||||
Ambient temp. & humid. range | +5℃ ~ +35℃ / <85%RH | ||||||
Testing Temperature | NSS ACSS 35℃±1℃ / CASS 50℃±1℃ | ||||||
Air Temperature | NSS ACSS 47℃±1℃ /CASS 63℃±1℃ | ||||||
Solution Consistence | NaCl 5% | ||||||
PH Value | NASS ACSS:6.5~7.2 / CASS:3.0~3.2 | ||||||
Temperature fluctuation | ≦±0.5℃ | ||||||
Temperature uniformity | ≦2. 0℃ | ||||||
Temperature deviation | ≦±2.0℃ | ||||||
Spray quantum | 1.0~2.0(ml/80cm2/h) | ||||||
Chamber Material | polyvinyl chloride (PVC) | ||||||
Heater | Corrosion-resistant titanium tube | ||||||
Temperature sensor | Platinum Resistance (PT-100) | ||||||
Safety device | Over-temperature protection , leakage protection |
Note:
1. The above specifications are for reference only, the actual specifications for the main quotation.
2. Custom made is available according to customers’ special requirements
ASTM G85 Annex 3 (A3) SWAAT test is a corrosion test that uses synthetic sea salt instead of traditional sodium chloride. The solution is then acidified using glacial acetic acid. This test is to be operated under wet bottom conditions.
Salt Solution: A synthetic sea salt solution made with the addition of glacial acetic acid.